We are the resin manufacturer you need!
Structures:Orthophthalic Resin
Processes:Hand lay-up
Application: Suitable for spray process and hand paste process, used for bonding and strengthening of acrylic /ABS sheet.
ZC-8222P resin is a phthalic pre-promoted unsaturated polyester resin with phthalic anhydride, maleic anhydride and standard diol as the main raw materials. It has low viscosity and medium reactivity.
ZC-8222P resin has high heat resistance, good water resistance, low temperature peak, good adhesion to acrylic /ABS board, easy to infiltrate glass fiber. Suitable for spray process and hand paste process, used for bonding and strengthening of acrylic /ABS sheet.
| Property | Value | Unit | TM |
| Appearance | Red turbidity Viscous liquid | – | – |
| Acid Value | 26-34 | mgKOH/g | GB/T 2895-2008 |
| Viscosity，25℃ | 0.18-0.21 | Pa.s | GB/T 7193-2008 |
| Solid Content | 53-61 | % | GB/T 7193-2008 |
| Thermal Stability,80℃ | ≥24 | h | GB/T 7193-2008 |
| Gelation time,25℃ | 8-18 | min | GB/T 7193-2008 |
| Property | Value | Unit | TM |
| Appearance | The casting body is free from defects | – | – |
| Babbitt Hardness | 40 | – | GB/T 3854-2005 |
| HDT | 60 | ℃ | GB/T 1634-2004 |
| Breake elongation | 1.8 | % | GB/T 2567-2008 |
| Tensile Strength | 50 | Mpa | GB/T 2567-2008 |
| Tensile modulus | 3600 | Mpa | GB/T 2567-2008 |
| Flexural strength | 80 | Mpa | GB/T 2567-2008 |
| Flexural modulus | 3600 | Mpa | GB/T 2567-2008 |
ZC-8222P resin contains accelerators, does not contain wax and thixotropic additives. due to the difference in the composition of acrylic /ABS sheet, the bond test should be carried out before use to ensure its applicability.
Net weight 220 kilograms, in metal drums. Special packaging requirements, please contact us.