We are the resin manufacturer you need!
Structures:Orthophthalic
Processes:Casting Resin
Application:t has been dissolved in cross-linking monomers such as styrene and has low viscosity and high reactivity.
ZC-2699R resin is an o-phthalic unsaturated polyester resin with phthalic anhydride, maleic anhydride and standard diol as main raw materials. It has been dissolved in cross-linking monomers such as styrene and has low viscosity and high reactivity
ZC-2699R resin has low viscosity, good wettability, and fast curing. The refractive index of its casting is close to that of alkali-free glass fiber. It has fast board running speed, good toughness, good light transmittance, and good divergence effect on direct sunlight. It is suitable for ordinary light-transmitting boards.
| Property | Value | Unit | TM |
| Appearance | Light yellow transparent viscous liquid | – | – |
| Acid Value | 16-24 | mgKOH/g | GB/T 2895-2008 |
| Viscosity，25℃ | 0.16-0.18 | Pa.s | GB/T 7193-2008 |
| Solid Content | 57-64 | % | GB/T 7193-2008 |
| Thermal Stability,80℃ | ≥24 | h | GB/T 7193-2008 |
| Gel time | 7-14 | min | GB/T 7193-2008 |
| Property | Value | Unit | TM |
| Appearance | Casting body has no defects | – | – |
| Barcol Hardness | 35 | – | GB/T 3854-2005 |
| HDT | 70 | ℃ | GB/T 1634-2004 |
| Break Elongation | 5 | Mpa | GB/T 2567-2008 |
| Tensile Strength | 60 | Mpa | GB/T 2567-2008 |
| Tensile Modulus | 2800 | Mpa | GB/T 2567-2008 |
| Flexural Strength | 100 | Mpa | GB/T 2567-2008 |
| Flexural Modulus | 3000 | Mpa | GB/T 2567-2008 |
| Property | Value | Unit | TM |
| Barcol Hardness | 330 | – | GB/T 3854-2005 |
| Tensile Strength | 18000 | Mpa | GB/T 1447-2005 |
| Tensile Modulus | 67 | Mpa | GB/T 1447-2005 |
| Flexural Strength | 16000 | Mpa | GB/T 1449-2005 |
| Flexural Modulus | 380 | Mpa | GB/T 1449-2005 |
1. ZC-2699R resin does not contain wax, accelerator or thixotropic agent.
2. ZC-2699R resin has moderate reactivity, and its board speed is generally 4-6m/min. To ensure product performance, the board speed should be set in combination with the actual state of equipment conditions and process conditions.
3. ZC-2699R resin is suitable for ordinary translucent tiles.
4. When selecting glass fiber, the refractive index of glass fiber and resin should be matched to ensure the light transmittance of the board.