We are the resin manufacturer you need!
Structures:DCPD
Processes:Casting Resin
Application:It has been dissolved in cross-linking monomers such as styrene, has low viscosity and moderate reactivity.
ZC-103A resin is based on dicyclopentadiene, maleic anhydride and standard diols DCPD type pre-accelerated thixotropic unsaturated polyester resin, which has been dissolved in cross-linking monomers such as styrene, has low viscosity and moderate reactivity.
ZC-103A resin contains wax, thixotropic auxiliaries and accelerators. ZC-103A resin is sensitive to light and easy to gel after seeing light, so it should be avoided to open the package or expose it to strong light before use.Thixotropic resin storage process thixotropic agent will gradually precipitate, is a normal phenomenon, should be fully stirred before use.
| Property | Value | Unit | TM |
| Appearance | Brown red viscous liquid | – | – |
| Acid Value | 17-23 | mgKOH/g | GB/T 2895-2008 |
| Viscosity，25℃ | 0.25-0.45 | Pa.s | GB/T 7193-2008 |
| Solid Content | 68-75 | % | GB/T 7193-2008 |
| Thermal Stability,80℃ | ≥24 | h | GB/T 7193-2008 |
| Gel time | 10-32 | min | GB/T 7193-2008 |
| Property | Value | Unit | TM |
| Appearance | Casting body has no defects | – | – |
| Barcol Hardness | 40 | – | GB/T 3854-2005 |
| HDT | 85 | ℃ | GB/T 1634-2004 |
| Break Elongation | 2 | Mpa | GB/T 2567-2008 |
| Tensile Strength | 50 | Mpa | GB/T 2567-2008 |
| Tensile Modulus | 3100 | Mpa | GB/T 2567-2008 |
| Flexural Strength | 90 | Mpa | GB/T 2567-2008 |
| Flexural Modulus | 3200 | Mpa | GB/T 2567-2008 |
| Property | Value | Unit | TM |
| Barcol Hardness | 65 | – | GB/T 3854-2005 |
| Tensile Strength | 330 | Mpa | GB/T 1447-2005 |
| Tensile Modulus | 16000 | Mpa | GB/T 1447-2005 |
| Flexural Strength | 330 | Mpa | GB/T 1449-2005 |
| Flexural Modulus | 16000 | Mpa | GB/T 1449-2005 |
ZC-103A resin contains wax, thixotropic auxiliaries and accelerators.
ZC-103A resin is sensitive to light and easy to gel after seeing light, so it should be avoided to open the package or expose it to strong light before use. Thixotropic resin storage process thixotropic agent will gradually precipitate, is a normal phenomenon, should be fully stirred before use.
Net weight is 220 kg, metal barrel.Please contact us for special packaging requirements.